Crack resistance of fiber‐reinforced asphalt mixtures: Effect of test specimen and test condition. Issue 3 (17th January 2022)

• Record Type: Journal Article
• Authors: Hajiloo, Hamid Reza; Karimi, Hamid Reza; Aliha, M. R. M.; Zanjirani Farahani, Hossein; Salehi, S. M.; Hajiloo, Mojtaba; Jafari Haghighatpour, Pegah
• Is Part Of: Fatigue & fracture of engineering materials & structures. Volume 45:Issue 3(2022)
• Page Start: 921
• Page End: 937
• Publication Date: 2022-01-17
• Subjects: asphalt concrete -- edge notch disc bend (ENDB) -- polyolefin aramid fiber -- pure mode I and II fracture toughness -- semicircular bend (SCB); Materials -- Fatigue -- Periodicals; Fracture mechanics -- Periodicals; 620.1123
• DOI: 10.1111/ffe.13647
• Languages: English
• ISSNs: 8756-758X

Abstract

Abstract: The effect of some important testing conditions including test specimen (SCB and ENDB), fracture mode (I and II), loading rate (0.5, 1.0, and 5.0 mm/min), and temperature (−5°C, −15°C, and −25°C) is evaluated on fracture toughness of asphalt material containing different percentages of fibers (0%, 0.025%, 0.05%, and 0.1% of unit weight). The experimental and numerical results show that the addition of 0.025%, 0.05%, and 0.1% of the polyolefin–aramid fiber in asphalt mixture increases the fracture toughness of the control mixture by about 8%, 17%, and 23% in pure mode I and 7%, 16%, and 24% in pure mode II, respectively; which are among the most promising enhancements compared to other fibers. Results also reveal that fracture toughness at mode I obtained from the SCB and ENDB specimens is similar. However, the mode II fracture toughness obtained from the ENDB specimen is about 12% higher than the corresponding value obtained from the SCB specimen. HIGHLIGHTS: The ability of ENDB was examined by comparing the result with the SCB specimen. Tests were performed using HMA asphalt concrete containing fiber content. Fracture toughness was measured for both pure mode I and II. The strengthening ability of used fiber was evaluated in comparison to other researches.