Effects of defects on fatigue behavior of TC17 titanium alloy for compressor blades: Crack initiation and modeling of fatigue strength. (January 2022)

• Record Type: Journal Article
• Authors: Chi, Weiqian; Wang, Wenjing; Xu, Wei; Li, Gen; Chen, Xin; Sun, Chengqi
• Is Part Of: Engineering fracture mechanics. Volume 259(2022)
• Publication Date: 2022-01
• Subjects: TC17 titanium alloy -- Surface defect -- Very high cycle fatigue -- Crack initiation -- Fatigue strength prediction; Fracture mechanics -- Periodicals; Rupture, Mécanique de la -- Périodiques; Fracture mechanics; Periodicals; 620.112605
• DOI: 10.1016/j.engfracmech.2021.108136
• Languages: English
• ISSNs: 0013-7944

Abstract

Highlights: S-N data of TC17 alloy with surface defects exhibits plateau region feature. Effects of defects on fatigue behavior are greatly related to the defect size. There is a critical defect size less than which it does not affect fatigue behavior. A model is developed to correlate the effects of defects on fatigue strength. The model is also validated by the results of metallic materials in literature. Abstract: S-N data of TC17 titanium alloy with surface defects exhibits plateau region (10 5 -10 9 cycles) feature. The effects of defects are greatly related to the defect size. When the defect size is bigger than the critical one, the crack initiates from the defect, and the fatigue strength σ w incorporating the effects of defects could be expressed as σ w = C area n, in which area denotes the square root of the projection area of defect perpendicular to the principal stress direction, C and n are parameters. The model is also validated by the experimental results of metallic materials in literature.