Insights into the impact of polydopamine modification on permeability and anti-fouling performance of forward osmosis membrane. (March 2022)

• Record Type: Journal Article
• Authors: Yang, Yi; Song, Chunyang; Wang, Pengcheng; Fan, Xinfei; Xu, Yuanlu; Dong, Guanming; Liu, Zhijian; Pan, Zonglin; Song, Yongxin; Song, Chengwen
• Is Part Of: Chemosphere. Volume 291:Part 1(2022)
• Publication Date: 2022-03
• Subjects: Forward osmosis (FO) -- Thin film composite (TFC) membrane -- Polydopamine (PDA) coating -- Position -- Anti-fouling; Pollution -- Periodicals; Pollution -- Physiological effect -- Periodicals; Environmental sciences -- Periodicals; Atmospheric chemistry -- Periodicals; 551.511
• DOI: 10.1016/j.chemosphere.2021.132744
• Languages: English
• ISSNs: 0045-6535

Abstract

Abstract: Forward osmosis (FO) has drawn wide attention as a promising method to address world-wide water crisis due to the advantages of low-energy consumption and easy separation operation. Unfortunately, the trade-off between permeability and selectivity as well as membrane fouling hindered the application of forward osmosis. Surface modification is a feasible method to address these issues. However, there is a lack of systematic evaluation about the effect of modification position on FO performance due to the asymmetric structure of thin film composite (TFC) FO membrane. To provide new insights into the design of FO membrane with satisfied permeability and fouling resistance, novel TFC FO membranes were fabricated by introducing polydopamine (PDA) on the support layer (TFC-I) or active layer (TFC-S), respectively. The surface morphology, chemical composition and wettability of the fabricated membrane were studied. It was found that the surface wettability of the modified membrane was improved greatly compared to pristine TFC membrane (TFC-C). Moreover, TFC-S membrane displayed a rougher surface than that of TFC-I membrane. As a result, a superior TFC-S membrane with a water flux of 60.95 ± 3.15 L m −2 h −1 in AL-DS mode was obtained, which was 72.61% and 17.87% higher than that of TFC-C and TFC-I membrane, respectively. In addition, the TFC-S membrane also presented an excellent fouling resistance and membrane regeneration performance during the three organic fouling cycle experiments. The results indicated that the introduction of PDA as a surface coating for TFC membranes modification guaranteed the high-performance and fouling resistance. Especially, the PDA coating on the support layer surface resulted in an enhancement in permeability, while both the permeability and anti-fouling performance were significantly improved with the PDA coating on the polyamide active layer surface. This study provides new insights into the development of modification TFC-FO membranes for practical applications in water treatment. Graphical abstract: Image 1 Highlights: The effect of PDA coating positions on performance of TFC membranes was studied. PDA coating greatly changed the roughness and wettability of the TFC membrane. The water flux of the membrane was greatly improved by introducing PDA coating. Better anti-fouling stability was obtained with PDA coating on PA layer surface.