Fabrication and characterisation of single-phase Hf2Al4C5 ceramics. Issue 4 (April 2022)

• Record Type: Journal Article
• Authors: Jayaseelan, Doni Daniel; Pramana, S.; Grasso, S.; Bai, Y.; Skinner, S.; Reece, M.J.; Lee, W.E.
• Is Part Of: Journal of the European Ceramic Society. Volume 42:Issue 4(2022)
• Page Start: 1292
• Page End: 1301
• Publication Date: 2022-04
• Subjects: Ternary carbides -- Hf2Al4C5 -- HRTEM -- Microstructure -- Oxidation -- Thermal conductivity; Ceramic materials -- Periodicals; Composite materials -- Periodicals; Matériaux céramiques -- Périodiques; Composites -- Périodiques; Ceramic materials; Composite materials; Periodicals; Electronic journals; 666.05
• DOI: 10.1016/j.jeurceramsoc.2021.12.035
• Languages: English
• ISSNs: 0955-2219

Abstract

Abstract: Single-phase Hf2 Al4 C5 ternary carbide was fabricated from Hf/Al/C powder mixtures by pressure assisted sintering techniques such as hot pressing and spark plasma sintering at 1900 °C for 3 h and 10 min, respectively. XRD confirmed that the ternary carbide started to form at temperatures as low as 1500 °C and with total formation of Hf2 Al4 C5 after reactive sintering for 1 h at 1900 °C. It is evident from HRTEM that two Hf-C layers were sandwiched with 4 Al-C layers (Al4 C3 ) in the Hf2 Al4 C5 ternary carbide. Tight interlocking of grains, faceted grains and stacking faults were occasionally observed. Thermal conductivity of Hf2 Al4 C5 is measured to be 14 w m −1 k −1 from room temperature to 1300 °C. The oxidation studies carried out at 1300 °C for 3 h reveal that the oxidation layer thickness is around 220 μm and it contains microcracks closer to sample surface whereas the interface looks seamless without any cracking or spallation of the oxide layer.