Experimental study and thermodynamic analysis on the selective oxidation of DP1180 dual‐phase steel. (2nd November 2021)

• Record Type: Journal Article
• Authors: Wang, Kun; Ding, Yuwen; Liu, Ya; Wang, Jianhua; Wu, Changjun; Tu, Hao; Peng, Haoping; Su, Xuping
• Is Part Of: Surface and interface analysis. Volume 54:Number 2(2022)
• Page Start: 117
• Page End: 125
• Publication Date: 2021-11-02
• Subjects: dual‐phase steel -- Fe–Mn–Cr–Si–C–O2 system -- selective oxidation -- thermodynamic calculation; Surfaces (Physics) -- Periodicals; Surface chemistry -- Periodicals; Thin films -- Periodicals; 541.33
• DOI: 10.1002/sia.7027
• Languages: English
• ISSNs: 0142-2421

Abstract

Abstract : The selective oxidation process of dual‐phase 1180 steel was investigated in this study. Annealing was carried out in Cr/Cr2 O3 Rhines pack at 820°C for 60, 120, and 240 s, under the oxygen partial pressures of 10 −23, 10 −25, and 10 −29 atm, respectively. Field emission scanning electron microscopy (FE‐SEM), electron backscattered diffraction (EBSD), and X‐ray photoelectron spectroscopy (XPS) were used to analyze the experimental results. The oxides involved SiO2, MnO, MnSiO3, Mn2 SiO4, and MnCr2 O4 . The amount of oxides augmented along with the increasing oxygen partial pressure. The Fe–Mn–Cr–Si–C–O2 oxidation diagram was calculated by thermodynamic software and was used to explain the selective oxidation process of dual‐phase 1180 steel. Experimental results combined with the thermodynamic computations well.