Leaching behavior of zinc and lead from electric arc furnace dust – Poly(vinyl) chloride residues after oxidative thermal treatment. (15th December 2021)

• Record Type: Journal Article
• Authors: Al-Harahsheh, Mohammad; Altarawneh, Sanad; Al-Omari, Mohammad; Altarawneh, Mohammednoor; Kingman, Sam; Dodds, Chris
• Is Part Of: Journal of cleaner production. Volume 328(2021)
• Publication Date: 2021-12-15
• Subjects: EAFD -- PVC -- Thermal decomposition -- Leaching -- Oxidation -- Zinc -- Lead; Factory and trade waste -- Management -- Periodicals; Manufactures -- Environmental aspects -- Periodicals; Déchets industriels -- Gestion -- Périodiques; Usines -- Aspect de l'environnement -- Périodiques; 628.5
• DOI: 10.1016/j.jclepro.2021.129622
• Languages: English
• ISSNs: 0959-6526

Abstract

Abstract: Oxidative thermal treatment of electric arc furnace dust (EAFD) mixed with poly(vinyl) chloride (PVC) was carried out to study the impact of oxidizing environment on the extraction of valuable metals. The effect of oxygen partial pressure, temperature and holding time of the thermal treatment, as well as the pH of the leaching solution were considered as operational variables in this study. HCl evolved during PVC decomposition was found to react with the metal oxides present in EAFD producing metal chlorides. It was found that thermal treatment above 350 °C caused significant vaporization of lead and zinc chlorides. After thermal treatment, the residue was leached in water, the cheapest available leaching reagent. Zinc and lead were extracted with recoveries up to ∼100%, while iron recovery was as low as 12.5% being suppressed by oxidation of ferrous iron. Operating under oxidative conditions supresses the post dissolution of iron in water by oxidizing Fe3 O4 to Fe2 O3 and by oxidizing any formed FeCl2 back to Fe2 O3 . The solution pH was also found to significantly affect the extraction of both lead and iron, especially at pH values above 4.0 where a sharp drop in metals recovery was observed. The obtained results present base for development of sustainable solution for treatment of PVC and EAFD wastes. Highlights: Oxidative thermal treatment (OTT) of EAFD:PVC at low temperature is proposed. OTT residue was water leached for metal extraction. OTT caused oxidation magnetite to hematite preventing its chlorination. Leaching of Zn and Pb can be achieved at high recoveries. Major Fe and carbon materials are left in residue for potential recycling.