Controllable dimensions and regular geometric architectures from self-assembly of lithium-containing polyhedral oligomeric silsesquioxane: Build for enhancing the fire safety of epoxy resin. (15th January 2022)

• Record Type: Journal Article
• Authors: Ye, Xinming; Zhang, Xiaolian; Jiang, Yunyun; Qiao, Liang; Zhang, Wenchao; Pan, Ye-Tang; Yang, Rongjie; Li, Jiarong; Li, Yingchun
• Is Part Of: Composites. Number 229(2022)
• Publication Date: 2022-01-15
• Subjects: M-POSS -- Self-assembly morphologies -- Epoxy resin -- Flame retardancy -- Mechanical properties; Composite materials -- Periodicals; Materials science -- Periodicals; Composite materials; Periodicals; Electronic journals; 620.118
• DOI: 10.1016/j.compositesb.2021.109483
• Languages: English
• ISSNs: 1359-8368

Abstract

Abstract: Mitigating the fire hazards of epoxy resin (EP) and simultaneously improving mechanical properties have always been a goal pursued by polymeric scientists. Herein, we prepared a lithium-containing hepta-isobutyl-POSS (ibu-T7 -Li-POSS). The chemical structure of ibu-T7 -Li-POSS was well characterized. Just via tuning the ethanol solution concentration, we can obtain zero-dimensional (0D) spherical nanoparticles, two-dimensional (2D) ultrathin mono-layer nanoflakes, three-dimensional (3D) multiple-layered lamellae and hexagonal petal-shaped micron-size crystal based on ibu-T7 -Li-POSS. Regular macroscopic octahedron single crystal of ibu-T7 -Li-POSS was analisized by single crystal X-ray diffraction. The prepared ibu-T7 -Li-POSS was incorporated into EP to improve the mechanical properties and enhance the fire safety. When the ibu-T7 -Li-POSS content was 1 wt%, the flexural strength of EP-1 was enhanced from 81.8 MPa of EP to 110 MPa. The incorporation of ibu-T7 -Li-POSS can apparently decrease the dielectric constant and loss of EP nanocomposites. Moreover, when 5 wt% of ibu-T7 -Li-POSS was incorporated into EP, the reduction of peak of heat release rate (p-HRR), peak of smoke production rate (p-SPR) and peak of CO production rate (p-COP) reached to 34.1%, 38.6% and 40.6%, respectively. Therefore, our findings provide a considerable promotion for the facile preparation of low-dimensional environment-friendly nano-/micron-flame retardants based on metal-containing polyhedral oligomeric silsesquioxane (M-POSS) compounds. Graphical abstract: Image 1 Highlights: A novel metal-POSS (ibu-T7 -Li-POSS) is firstly synthesized via one-pot method. Controllable dimensional ibu-T7 -Li-POSS nano-/micron-crystals are fabricated. Thermal stability and mechanical properties of EP nanocomposites are improved by introducing ibu-T7 -Li-POSS. Ibu-T7 -Li-POSS apparently reduces fire hazards of the formed EP nanocomposites. The mechanism of catalytic charring of lithium for EP is illustrated in detail.