Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys. (26th October 2021)

• Record Type: Journal Article
• Authors: Xue, Heng; Lyu, Jinbei; Wang, Fengxue; Liao, Hongxin; Kim, Jonghyun; Pan, Fusheng
• Other Names: Ares Alicia E. Academic Editor.
• Is Part Of: Advances in materials science and engineering. Volume 2021(2021)
• Publication Date: 2021-10-26
• Subjects: Materials science -- Periodicals; Materials science; Periodicals; 620.11
• DOI: 10.1155/2021/8922503
• Languages: English
• ISSNs: 1687-8434

Abstract

Abstract : The microstructures of Mg96 Y2 Zn2, Mg96 Y2 Zn1 Co1, Mg96 Y2 Zn1 Ni1, and Mg96 Y2 Zn1 Co0.5 Ni0.5 (at.%) alloys were investigated by XRD, SEM/EDS, and TEM. The α -Mg matrix, the long-period stacking ordered (LPSO) phase, and the bright compounds were observed in the as-cast alloys. The ability of Co to form LPSO phase with Mg and Y is weaker than that of Zn, but it can produce some new intermetallic compounds. The effect of Ni on phase content of alloys was opposite to that of Co. After replacing partial Zn with Co and Ni, the increase in the LPSO phase is more obvious than that of Co or Ni alone to replace partial Zn. The ability to form LPSO phase with Mg and Y atoms in Mg-Y-TM alloys can be ranked as follows: Co-Ni > Ni > Zn > Co. From the point-of-view of mechanical performance, the substitution of Co-Ni for partial replacement of Zn exhibited the best yield strength; the tensile yield strength, ultimate tensile strength, compressive yield stress, and ultimate compressive stress of which were 345 MPa, 453 MPa, 335 MPa, and 470 MPa, respectively. However, the ductility did not improve significantly.