Forming Hard Anodic Films on Aluminum by Anodization in Oxalic Acid and Alcohol. Issue 10 (20th October 2021)

• Record Type: Journal Article
• Authors: Asoh, Hidetaka; Sano, Takuma
• Is Part Of: Journal of the Electrochemical Society. Volume 168:Issue 10(2021)
• Publication Date: 2021-10-20
• Subjects: Anodic Films -- Anodizing -- Electrochemical Engineering; Electrochemistry -- Periodicals; 541.3705
• DOI: 10.1149/1945-7111/ac2ec1
• Languages: English
• ISSNs: 0013-4651

Abstract

Abstract : Porous anodic films have attracted wide attention because of their potential applications in various industrial fields. Reducing their porosity is expected to improve the hardness. This study focused on evaluating the effect of the electrolyte composition on the hardness of anodic alumina films formed on aluminum by anodization under mild conditions. In particular, the effect of adding alcohol (i.e., ethanol and ethylene glycol) to an oxalic acid–based electrolyte was considered. The voltage–time curve, coating ratio (i.e., film formation efficiency), morphology, and Martens hardness of the resulting anodic alumina films were clearly affected by the type and amount of added alcohol. Adding alcohol effectively suppressed the chemical dissolution of the anodic film during anodization without needing to lower the electrolyte temperature, which formed high-strength films with low porosity and thick pore walls. The Martens hardness of the formed films increased by 18% with the addition of 50 vol% ethanol and increased by 25% with the addition of 50 vol% ethylene glycol.