Comparison between CaO- and MgO-activated ground granulated blast-furnace slag (GGBS) for stabilization/solidification of Zn-contaminated clay slurry. (January 2022)

• Record Type: Journal Article
• Authors: Zhang, Yunhui; Ong, Yi Jie; Yi, Yaolin
• Is Part Of: Chemosphere. Volume 286:Part 3(2022)
• Publication Date: 2022-01
• Subjects: Lime -- Reactive magnesia -- GGBS -- Stabilization/solidification -- Dredged contaminated sediment; Pollution -- Periodicals; Pollution -- Physiological effect -- Periodicals; Environmental sciences -- Periodicals; Atmospheric chemistry -- Periodicals; 551.511
• DOI: 10.1016/j.chemosphere.2021.131860
• Languages: English
• ISSNs: 0045-6535

Abstract

Abstract: Stabilization/solidification (S/S) is a low-cost and effective remedial technique for dredged contaminated sediments. Quick lime (CaO)-activated and reactive magnesia (MgO)-activated ground granulated blast furnace slag (GGBS) are effective and low-carbon S/S binders. However, the existence of metals, especially Zn, in contaminated sediments, may hinder the hydration of GGBS. This study compared the performance and mechanisms of CaO-GGBS, MgO-GGBS and ordinary Portland cement (OPC) for the treatment of Zn-contaminated clay slurry using unconfined compressive strength (UCS) test, one-stage batch leaching test, and mineralogical and thermal analyses. The results showed that the application of the MgO-GGBS (GGBS dosage of 10 % and MgO of 0 %–3 % (of dry clay by mass)) had positive effects on the mechanical strength and Zn immobilization of the contaminated clay slurry while the CaO-GGBS affected negatively and the situation became even worse at a higher CaO dosage (0 %–1.5 % of dry clay by mass). In comparison with OPC, the application of MgO-GGBS produced higher mechanical strength and that for CaO-GGBS was the lowest. The Zn leaching difference depends on initial Zn concentrations. X-ray diffraction (XRD) and thermogravimetric analysis (TGA) results showed that a retarder, calcium zinc hydroxide, formed in the immobilization process when adding the CaO-GGBS binder, hindering the GGBS hydration and further leading to inferior strength and higher Zn leachability. The clay slurry treated by the MgO-GGBS binder was found to have a higher calcium silicate hydrate content which explained its high strength and low leachability. Highlights: The S/S mechanisms of MgO- and CaO-GGBS were systematically compared and clarified. A retarder calcium zinc hydroxide was formed when using CaO-GGBS binder. Zn immobilization in contaminated clay slurry is largely pH-dependent. Compared with GGBS, CaO-GGBS reduced strength of S/S sample while MgO-GGBS increased.