Tensile and stressed-oxidation behavior of 2D SiC/BN/SiC composites at Intermediate Temperatures in Air. Issue 1 (1st January 2022) - Han, Xiao
Abstract: The stressed-oxidation behavior of 2D CVI SiC/BN/SiC composites was studied at intermediate temperatures (800 °C) in air. The ultimate tensile strength (UTS) was acquired to determine the constant stress. The results show that the UTS at intermediate temperature is 14.3 % lower than that at room temperature. The strain-time curves at all stress levels show a deceleration stage and a stable stage. The stressed-oxidation rupture life decreases from 5.4 h to 0.9 h when the stress increases from 60 % to 90 % of the UTS. The element composition and fracture morphologies of the composites were also analyzed. The results show that the oxidation degree increases as the rupture time increases or constant stress decreases. Fiber degradation and interface defects caused by component oxidation induced local fiber failure and ultimate rupture of the composites, which may be attributed to strength degradation at intermediate temperatures and rupture of the composites during stress oxidation.