Renewable and recyclable covalent adaptable networks based on bio-derived lipoic acid. Issue 40 (28th September 2021)

• Record Type: Journal Article
• Authors: Alraddadi, Maher A.; Chiaradia, Viviane; Stubbs, Connor J.; Worch, Joshua C.; Dove, Andrew P.
• Is Part Of: Polymer chemistry. Volume 12:Issue 40(2021)
• Page Start: 5796
• Page End: 5802
• Publication Date: 2021-09-28
• Subjects: Polymers -- Periodicals; Macromolecules -- Periodicals; Polymerization -- Periodicals; 547.705
• DOI: 10.1039/d1py00754h
• Languages: English
• ISSNs: 1759-9954

Abstract

Abstract : Lipoic acid provides a modular and bio-sourced platform from which the create covalent adaptable network materials. Abstract : The modern materials economy is inefficient since most products are principally derived from non-renewable feedstocks and largely single-use in nature. Conventional thermoset materials are often inherently unreprocessable due to their irreversible covalent crosslinks and hence are challenging to recycle and/or reprocess. Covalent adaptable networks (CAN)s, which incorporate reversible or dynamic covalent bonding, have emerged as an efficient means to afford reprocessable crosslinked materials and increasing the feedstock sustainability of CANs is a developing aim. In this study, the biomass-derived lipoic acid, which possesses a dynamic cyclic disulfide moiety, was transformed into a series of bifunctional monomers via a one-step esterification or amidation reaction and reacted with a commercially available multi-valent thiol in the presence of an organobase catalyst to afford dynamically crosslinked networks. Large differences in material properties, such as storage modulus and glass transition temperature, were observed when the ratio of the lipoic acid-based monomer to thiol (from 1 : 1 to 16 : 1) and the composition of the monomer were changed to modify the network architecture. The thermomechanical properties of an optimised formulation were investigated more thoroughly to reveal a moderately strong rubber (ultimate tensile strength = 1.8 ± 0.4 MPa) possessing a large rubbery plateau (from 0 to 150 °C) which provides an adaptable material with a wide operational temperature range. Finally, the chemical recycling, or depolymerisation, of the optimised network was also demonstrated by simply solvating the material in the presence of an organobase catalyst.