Failure investigation of a 304 stainless steel geothermal tube. (November 2021)

• Record Type: Journal Article
• Authors: Liu, Menghao; Ni, Zhuoyan; Du, Cuiwei; Liu, Zhiyong; Sun, Meihui; Fan, Endian; Wang, Qiuyu; Yang, Xiaojia; Li, Xiaogang
• Is Part Of: Engineering failure analysis. Volume 129(2021)
• Publication Date: 2021-11
• Subjects: Geothermal water convection tube -- Intergranular corrosion -- Stress corrosion cracking; System failures (Engineering) -- Periodicals; Fracture mechanics -- Periodicals; Reliability (Engineering) -- Periodicals; Pannes -- Périodiques; Rupture, Mécanique de la -- Périodiques; Fiabilité -- Périodiques; Fracture mechanics; Reliability (Engineering); System failures (Engineering); Periodicals; Electronic journals; 620.112
• DOI: 10.1016/j.engfailanal.2021.105694
• Languages: English
• ISSNs: 1350-6307

Abstract

Graphical abstract: Highlights: Branching cracks reveal the failure was attributed to stress corrosion cracking. Initiation of SCC cracks mainly results from intergranular corrosion. The SCC cracks propagated in a mixed mode of TGSCC and IGSCC. Sensitized material, chloride and residual stress lead to the SCC failure synthetically. Abstract: The investigation of this paper aimed at finding the failure cause of a heavily cracked geothermal water convection tube, utilizing electron backscattered diffraction, double loop potentiodynamic polarization test, and energy-dispersive X-ray spectroscopy. Results show the failure was attributed to stress corrosion cracking (SCC). Chloride in the service environment has induced the initiation of SCC cracks. The sensitization of matrix increased the susceptibility to intergranular cracking, which may result from improper heat treatment before service. The residual stress arising from the manufacturing process promoted the failure process. The SCC cracks originated from the internal tube. In the early stage, the cracks propagated along austenite grain boundaries. Thereafter, they transformed into a coexisting mode of intergranular cracking and transgranular cracking. The failure was attributed to the synthetical effect of sensitization, chloride, and residual stress.