High thermoelectric power factor in Cu–Ni alloy originate from potential barrier scattering of twin boundaries. (October 2015)

• Record Type: Journal Article
• Authors: Mao, Jun; Wang, Yumei; Kim, Hee Seok; Liu, Zihang; Saparamadu, Udara; Tian, Fei; Dahal, Keshab; Sun, Jingying; Chen, Shuo; Liu, Weishu; Ren, Zhifeng
• Is Part Of: Nano energy. Volume 17(2015:Oct.)
• Page Start: 279
• Page End: 289
• Publication Date: 2015-10
• Subjects: Thermoelectric -- Cu–Ni alloy -- Nanoscale twins -- Potential barrier scattering; Nanoscience -- Periodicals; Nanotechnology -- Periodicals; Nanostructured materials -- Periodicals; Power resources -- Technological innovations -- Periodicals; Nanoscience; Nanostructured materials; Nanotechnology; Power resources -- Technological innovations; Periodicals; 621.042
• DOI: 10.1016/j.nanoen.2015.09.003
• Languages: English
• ISSNs: 2211-2855

Abstract

Abstract: Constantan alloy (Cu–Ni) has been known for a long time in thermocouples due to its thermal power property. In this study, we show an enhancement in thermoelectric performance of Cu56 Ni42 Mn2 alloy by introducing nanoscale twins into its microstructure. Comparing to arc-melted ingot (without nanoscale twins), the ball milled and hot pressed (BM–HP) samples with twinning showed a higher Seebeck coefficient of ~−72.5 μV K −1 (an increase of ~12% at 873 K), a larger power factor of ~102 μW cm −1 K −2 (an increase of ~21% at 873 K), and hence a higher ZT of ~0.19 (an increase of ~34% at 873 K). A high output power density of ~53.4 W cm −2 is calculated from the high power factor even though the conversion efficiency is lower than 3% due to the low ZT . TEM characterization shows there is a large quantity of nanoscale twins with spacing of 50–200 nm. It is very likely that low-energy carriers are selectively scattered by the twin boundaries ( i.e., potential barrier scattering) thus lead to enhanced Seebeck coefficient. The improved thermoelectric performance of nano-twinned Cu–Ni alloy suggests constantan could be promising in thermoelectric power generation where the power output density is more important than the conversion efficiency. Graphical abstract: Highlights: Thermoelectric properties of arc-melted Cu–Ni ingot and ball-milled hot pressed Cu–Ni samples are characterized. The potential barrier scattering by the nanoscale twins are discussed. Energy conversion efficiency and output power are calculated by engineering figure of merit ( ZT ) eng and power factor ( PF ) eng .