Effect of rare earth nucleating agent on supercritical CO2 foaming behavior of block copolymerized polypropylene. Issue 2 (March 2022)

• Record Type: Journal Article
• Authors: Zhang, Yun; He, Yadong; Xin, Chunling; Su, Yanbin
• Is Part Of: Cellular polymers. Volume 41:Issue 2(2022)
• Page Start: 53
• Page End: 79
• Publication Date: 2022-03
• Subjects: Polypropylene -- rare earth nucleating agent -- β-crystal -- crystallization -- foam; Plastic foams -- Periodicals; Foam rubber -- Periodicals; 620.192
• DOI: 10.1177/02624893211053678
• Languages: English
• ISSNs: 0262-4893

Abstract

The rare earth nucleating agent was used to modify block copolymerized polypropylene (PPB) in foaming process. The results show that the crystallization of PPB and the melting temperature of β-crystal increased gradually with increased β-crystal nucleating agent content. The total crystallinity decreased with amount of addition increasing, and the relative content of β-crystal increased first and then decreased. When β-crystal nucleating agent content was 0.4 wt%, the relative β-crystal content reached the maximum value of 95.27%, and the final crystal grain refinement significantly. The addition of rare earth β-crystal nucleating agent has a good effect on improving the uniformity of foam cells. Under the same content of β-crystal nucleating agent and pressure, the average cell diameter and expansion ratio increased with the saturation temperature increasing. After the foaming temperature reaches 155°C, the expansion ratio began to decrease, which was also consistent with the changed trend of relative β-crystal content. At the same content of temperature and relative β-crystal, as the foaming pressure increased, the cell diameter decreased gradually, and the expansion ratio increased first, and then decreased.