Flexible high-energy and stable rechargeable vanadium-zinc battery based on oxygen defect modulated V2O5 cathode. (September 2021)

• Record Type: Journal Article
• Authors: Liang, Xinyue; Yan, Lijin; Li, Wenpo; Bai, Youcun; Zhu, Chong; Qiang, Yujie; Xiong, Bingxue; Xiang, Bin; Zou, Xuefeng
• Is Part Of: Nano energy. Volume 87(2021)
• Publication Date: 2021-09
• Subjects: Aqueous electrolytes -- Battery -- Durability -- Vanadium -- High voltage -- Zinc; Nanoscience -- Periodicals; Nanotechnology -- Periodicals; Nanostructured materials -- Periodicals; Power resources -- Technological innovations -- Periodicals; Nanoscience; Nanostructured materials; Nanotechnology; Power resources -- Technological innovations; Periodicals; 621.042
• DOI: 10.1016/j.nanoen.2021.106164
• Languages: English
• ISSNs: 2211-2855

Abstract

Abstract: The development of earth-abundant, high-capacity and stable cathode materials for robust aqueous Zn-ion batteries (ZIBs) is an ongoing challenge. With the merits of suitable operating voltage window and highly reversible redox reaction, vanadium oxide has recently emerged as an attractive cathode material. Herein, an oxygen defect modulated binder-free V2 O5 nanorods (named as PVO@C) was constructed for aqueous/quasi-solid-state Zn ion battery. Accompanying the fast electron transport ability, increased concentration of oxygen defect and enhanced active sites, the aqueous PVO@C//Zn battery delivers an excellent high capacity of 385.34 mAh g −1 at 0.13 A g −1 and robust long-term life span of 86.7% capacity retention after 5000 cycles with nearly 100% coulomb efficiency. In particular, the assembled quasi-solid-state ZIBs exhibited the high voltage of 1.3 V, yielding an admirable energy density of 10.5 mWh cm −3 at a power density of 33.4 mW cm −3 and admirable cycling performance. What's more, the solid-state ZIB exhibits extremely high safety, wettability and wear-ability over the lithium ion batteries. It performs well even at a variety of severe hazardous conditions, such as punctured, soaked, bent, sewed, washed, cut, and hammered conditions. This work innovatively proposes the synergistic effect of oxygen defect modulation and phosphorus doping to optimize reaction kinetics, which will lead to further improvements in the performance of metal oxides electrode. This strategy can be extended to electrode materials of other battery systems for the construction of highly efficient flexible energy storage devices and accelerated the commercialization of wearable electronics technology. Graphical Abstract: ga1 Highlights: An facile hydrothermal method is used to synthesis a binder-free electrode material of PVO@C nanorods. After the introduction of oxygen defects and phosphor doping, the conductivity and capacity have been considerable improvement. The robust PVO@C//Zn battery demonstrates an excellent capacity of 385.34 mA h g −1 and a long-term cyclability of 86.7% capacity retention after 5000 cycles. A flexible and high capacitance quasi solid-state PVO@C//Zn battery (SS ZIB) is assembled, achieving an excellent volumetric energy density (10.5 mW h cm −3 ) at volumetric power density (33.4 mW cm −3 ) together with a stable cycling capability. This SS ZIB manifests an extremely high safety, wettability and wear-ability though working well in a variety of safety related experiments, further proving its wide application prospect.