In situ synthesis of high dielectric constant GNPs/PBO nanocomposites with enhanced thermostability. Issue 3 (28th May 2019)

• Record Type: Journal Article
• Authors: Chen, Yi; Kong, Zhen; Chen, Wenqi; Xiao, Lv; Yuan, Yong; Li, Zhongquan; Zhuang, Qixin
• Is Part Of: IET nanodielectrics. Volume 2:Issue 3(2019:Oct.)
• Page Start: 97
• Page End: 102
• Publication Date: 2019-05-28
• Subjects: nanocomposites -- casting -- tensile strength -- X‐ray diffraction -- polymerisation -- polymers -- thermal stability -- graphene -- graphite -- permittivity -- scanning electron microscopy -- nanoparticles -- nanofabrication -- filled polymers -- dielectric polarisation -- thin films; solution casting method -- sand core plates -- PBO matrix -- GNPs fillers -- pristine PBO polymer -- polymerisation -- high dielectric constant GNPs‐PBO nanocomposites -- conductive filler‐polymer system -- interfacial polarisation -- tensile strength -- graphene nanosheets -- XRD -- interlayer spacing -- methanesulfonic acid -- MSA -- poly(p‐phenylene benzobisoxazole) matrix -- graphite nanoparticles -- thermostability -- temperature 630.0 degC -- pressure 258.0 MPa; Dielectrics -- Periodicals; Nanoelectronics -- Periodicals; 537.24
• DOI: 10.1049/iet-nde.2019.0002
• Languages: English
• ISSNs: 2514-3255

Abstract

Abstract : Graphite nanoparticles (GNPs) were introduced into poly(p‐phenylene benzobisoxazole) (PBO) matrix to produce composites via in situ polymerisation. Films of various composites were fabricated through the solution casting method in methanesulfonic acid (MSA) with the help of two sand core plates. The interlayer spacing of GNPs increased slightly confirmed by XRD as a result of an expanding effect caused by continuously formed PBO chains between the graphene nanosheets of GNPs during polymerisation. Also, due to the uniform dispersion of GNPs into PBO matrix, composite films exhibited an improved tensile strength (258 MPa, 72% higher than that of pure PBO) with 5 wt% loading of GNPs fillers. The initial decomposition temperature of the composite is ∼630°C. Besides, benefitting from the interfacial polarisation in this conductive filler/polymer system, the dielectric constant of the composites with 10 wt% loading of GNPs reached 6.96, which were over two times higher than that of pristine PBO polymer (2.91).