Indium doped ZnO nano-powders prepared by RF thermal plasma treatment of In2O3 and ZnO. (26th May 2015)

• Record Type: Journal Article
• Authors: Lee, Mi-Yeon; Song, Min-Kyung; Seo, Jun-Ho; Kim, Min-Ho
• Is Part Of: Japanese journal of applied physics. Volume 54:Number 6(2015:Jun.)
• Publication Date: 2015-05-26
• Subjects: Physics -- Periodicals; 621.05
• DOI: 10.7567/JJAP.54.065201
• Languages: English
• ISSNs: 0021-4922

Abstract

Abstract: Indium doped ZnO nano-powders were synthesized by the RF thermal plasma treatment of In2 O3 and ZnO. For this purpose, micron-sized ZnO powder was mixed with In2 O3 powder at the In/Zn ratios of 0.0, 1.2, and 2.4 at. % by ball milling for 1 h, after which the mixtures were injected into RF thermal plasma generated at the plate power level of ∼140 kV A. As observed from the field emission scanning electron microscopy (FE-SEM) images of the RF plasma-treated powders, hexagonal prism-shaped nano-crystals were mainly obtained along with multi-pod type nano-particles, where the number of multi-pods decreased with increasing In/Zn ratios. In addition, the X-ray diffraction (XRD) data for the as-treated nano-powders showed the diffraction peaks for the In2 O3 present in the precursor mixture to disappear, while the crystalline peaks for the single phase of ZnO structure shifted toward lower Bragg angles. In the UV–vis absorption spectra of the as-treated powders, redshifts were also observed with increases of the In/Zn ratios. Together with the FE-SEM images and the XRD data, the redshifts were indicative of the doping process of ZnO with indium, which took place during the RF thermal plasma treatment of In2 O3 and ZnO.