A green method to reduce graphene oxide with carbonyl groups residual for enhanced electrochemical performance. (July 2018) - Yu, Mengying
Abstract: Reduced graphene oxide nanosheets modified with rich carbonyl groups (C=O) was obtained through a facile dehydration process by making use of the synergistic effect between phosphoric acid and monosodium phosphate. The product exhibited a high specific capacitance of 413 F g −1 at the current density of 0.25 A g −1 mainly owing to the high percentage of retained C=O groups which provided reversible pseudocapacitance and favored good dispersion. Additionally, the symmetric supercapacitors based on the modified graphene nanosheets showed high specific capacitance (314.2 F g −1 at 1 A g −1 ) and superior electrochemical stability with only 5.8% loss of its initial specific capacitance after 10000 cycle tests (at the current densities of 5 A g −1 ). The present work proposed an environmentally friendly way in controlling surface structure of reduced graphene oxide which promises great potential of graphene-based electrode materials for high performance energy-storage devices. Graphical abstract: Graphene nanosheets decorated with superior carbonyl groups (C=O) was obtained via a green method in the medium of dilute H3 PO4 and NaH2 PO4 . During this process, almost all the C=O group in graphene oxide were retained, featuring excellent pseudocapacitive performance. Under the current density of 0.5 and 1A g −1, the specific capacitance of the electrode reached 413, 374F g −1, respectively. Image 1