Sintering behaviour and microwave dielectric properties of BaAl2−2x(ZnSi)xSi2O8 ceramics. Issue 4 (April 2018) - Song, Xiao-Qiang
Abstract: BaAl2−2 x (ZnSi) x Si2 O8 ( x = 0.2–1.0) ceramics were prepared using the conventional solid-state reaction method. The sintering behaviour, phase composition and microwave dielectric properties of the prepared compositions were then investigated. All compositions showed a single phase except for x = 0.8. By substituting (Zn0.5 Si0.5 ) 3+ for Al 3+ ions, the optimal sintering temperatures of the compositions decreased from 1475 °C ( x = 0) to 1000 °C ( x = 0.8), which then slightly increased to 1100 °C ( x = 1.0). Moreover, the phase stability of BaAl2 Si2 O8 was improved. A novel BaZnSi3 O8 microwave dielectric ceramic was obtained at the sintering temperature of 1100 °C. This ceramic possesses good microwave dielectric properties with ε r = 6.60, Q × f = 52401 GHz (at 15.4 GHz) and τ f = −24.5 ppm/°C.