Influence of porosity on mechanical properties of tetragonal stabilized zirconia. Issue 4 (April 2018)

• Record Type: Journal Article
• Authors: Boccaccini, Dino N.; Frandsen, Henrik Lund; Soprani, S.; Cannio, Maria; Klemensø, Trine; Gil, Vanesa; Hendriksen, Peter Vang
• Is Part Of: Journal of the European Ceramic Society. Volume 38:Issue 4(2018)
• Page Start: 1720
• Page End: 1735
• Publication Date: 2018-04
• Subjects: Yttria stabilized zirconia -- Porosity -- Mechanical properties -- Anode supported solid oxide fuel cell; Ceramic materials -- Periodicals; Composite materials -- Periodicals; Matériaux céramiques -- Périodiques; Composites -- Périodiques; Ceramic materials; Composite materials; Periodicals; Electronic journals; 666.05
• DOI: 10.1016/j.jeurceramsoc.2017.09.029
• Languages: English
• ISSNs: 0955-2219

Abstract

Highlights: Loss of transformation toughening and R-curve effect for high porosities (>50%). First measurement of R-curve in porous 3YSZ. Increase of flaw tolerance for higher porosities. Abstract: 3YSZ specimens with variable open porosity (1–57%) were fabricated, and the stiffness, strength and fracture properties (fracture toughness and R-curve) were measured to investigate their potential use as support structures for solid oxide fuel or electrolysis cells. The ball-on-ring test was used to characterize Young's modulus and Weibull strength. The variation of fracture toughness with porosity was investigated and modelled using the results from fracture mechanical testing. A distinct R-curve behaviour was observed in dense 3YSZ specimens, in samples with a porosity around 15% and in some of the highly porous samples (porosities ∼45%) reflecting a transformation toughening in the material. For the most porous samples, the "R-curve behaviour" disappeared and subcritical crack growth was observed. The studies indicate that even highly porous 3YSZ structures (porosities exceeding 40%) are feasible supports for SOFC/SOECs from a mechanical point of view.