Calcareous smectite clay as a pozzolanic alternative to kaolin. Issue 9 (26th July 2021)

• Record Type: Journal Article
• Authors: Danner, Tobias; Norden, Geir; Justnes, Harald
• Is Part Of: European journal of environmental and civil engineering. Volume 25:Issue 9(2021)
• Page Start: 1647
• Page End: 1664
• Publication Date: 2021-07-26
• Subjects: Pozzolana -- cement -- hydration -- in-situ XRD -- compressive strength; Sustainable engineering -- Periodicals; Civil engineering -- Environmental aspects -- Periodicals; Environmental engineering -- Periodicals; 628
• DOI: 10.1080/19648189.2019.1590741
• Languages: English
• ISSNs: 1964-8189

Abstract

Abstract: The hydration of cement pastes with addition of a kaolinite rich clay (Clay A) and a calcareous smectite rich clay (Clay B) was investigated with isothermal calorimetry, in-situ XRD, PXRD, TGA and EPMA. Portland cement was replaced by 20, 35 and 50 weight% calcined clay in cement pastes and mortars. Both clays showed good pozzolanic reactivity. However, clay A having a higher amount of metakaolin and higher specific surface was more reactive in terms of CH consumption and mortar strength development. 50% replacement of PC by calcined Clay A resulted in increased 28 day compressive strength while mortars with 50% calcined Clay B showed almost equal 28 day compressive strength compared to the reference. With increasing addition of calcined clay, the second aluminate reaction (formation of AFm phase) of cement hydration was accelerated and the cement pastes became under sulphated. This resulted in a stronger and earlier sulphate depletion peak, especially in pastes with calcined Clay A. Due to 3% calcite in the used cement the main hydration product found was carboaluminate hydrate. The favoured formation of carboaluminate hydrate stabilised ettringite in the cement pastes.