Synthesis and Evaluation of a Water-Soluble Hyperbranched Polymer as Enhanced Oil Recovery Chemical. (27th November 2013)

• Record Type: Journal Article
• Authors: Lai, Nanjun; Qin, Xiaoping; Ye, Zhongbin; Peng, Qin; Zhang, Yan; Ming, Zheng
• Other Names: Pitsikalis Marinos Academic Editor.
• Is Part Of: Journal of chemistry. Volume 2013(2013)
• Publication Date: 2013-11-27
• Subjects: Chemistry -- Periodicals; 540.5
• DOI: 10.1155/2013/824785
• Languages: English
• ISSNs: 2090-9063

Abstract

Abstract : A novel hyperbranched polymer was synthesized using acrylamide (AM), acrylic acid (AA), N -vinyl-2-pyrrolidone (NVP), and dendrite functional monomer as raw materials by redox initiation system in an aqueous medium. The hyperbranched polymer was characterized by infrared (IR) spectroscopy, 1 H NMR spectroscopy, 13 C NMR spectroscopy, elemental analysis, and scanning electron microscope (SEM). The viscosity retention rate of the hyperbranched polymer was 22.89% higher than that of the AM/AA copolymer (HPAM) at 95°C, and the viscosity retention rate was 8.17%, 12.49%, and 13.68% higher than that of HPAM in 18000 mg/L NaCl, 1800 mg/L CaCl2, and 1800 mg/L MgCl2 ·6H2 O brine, respectively. The hyperbranched polymer exhibited higher apparent viscosity (25.2 mPa·s versus 8.1 mPa·s) under 500 s −1 shear rate at 80°C. Furthermore, the enhanced oil recovery (EOR) of 1500 mg/L hyperbranched polymer solutions was up to 23.51% by the core flooding test at 80°C.