Three different recycle codes of plastic/Acacia fibre composites: physical and morphological properties. Issue 1 (2nd January 2019)

• Record Type: Journal Article
• Authors: Gulitah, Verra; Liew, Kang Chiang
• Is Part Of: International journal of biobased plastics. Volume 1:Issue 1(2019)
• Page Start: 1
• Page End: 7
• Publication Date: 2019-01-02
• Subjects: High density polyethylene -- low density polyethylene -- polypropylene -- physical properties -- plastic content -- wood fibre; Thermoplastics -- Periodicals; Elastomers -- Periodicals; Thermosetting plastics -- Periodicals; Thermosetting plastics; Thermoplastics; Elastomers; Biodegradable plastics; Periodicals; 668.4
• DOI: 10.1080/24759651.2018.1557585
• Languages: English
• ISSNs: 2475-9651

Abstract

ABSTRACT: In this study, the term wood-plastic composite (WPC) refers to three different recycle codes of plastics combine with Acacia fiber namely polypropylene-wood fiber (PP-WF), high density polyethylene-wood fiber (HDPE-WF), and low density polyethylene-wood fiber (LDPE-WF). Each WPC was produced at different percentage combination (100:0, 90:10, 80:20, 70:30, 60:40, and 50:50). The relationship between plastic content and the physical properties (water absorption, thickness swelling, and density) of WPC were investigated. Water absorption and thickness swelling were evaluated after 15 days of water immersion. It was found that WPC of PP-WF, HDPE-WF and LDPE-WF had a significant difference at P ≤ 0.05 for water absorption, thickness swelling, and density. While water absorption and thickness swelling increased when the plastic content decreased. At combination of 50:50, WPC of PP-WF, HDPE-WF, and LDPE-WF showed range value between 52.03% and 56.27% of water absorption. While for thickness swelling at combination of 50:50 WPC of PP-WF showed 4.62%, HDPE-WF and LDPE-WF showed 4.61% and 4.77%, respectively. WPC of PP-WF, HDPE-WF, and LDPE-WF showed density 1.033 g/cm 3, 0.862 g/cm 3, and 0.870 g/cm 3 respectively, at 100% plastic content. This finding revealed due to the present of hydroxyl group in wood fiber and some voids in WPC. The evidence of the poor interfacial bonding in WPC was analyzed using scanning electron microscope.