Nanoparticle formation and emission during laser ablation of ceramic tiles. (December 2018)

• Record Type: Journal Article
• Authors: Salmatonidis, Apostolos; Viana, Mar; Pérez, Noemí; Alastuey, Andrés; de la Fuente, Germán F.; Angurel, Luis Alberto; Sanfélix, Vicenta; Monfort, Eliseo
• Is Part Of: Journal of aerosol science. Volume 126(2018)
• Page Start: 152
• Page End: 168
• Publication Date: 2018-12
• Subjects: Nanoparticles -- Ceramic industry -- Laser ablation -- Formation mechanisms; Aerosols -- Periodicals; Aerosols -- Periodicals; Aérosols -- Périodiques; 541.34515
• DOI: 10.1016/j.jaerosci.2018.09.006
• Languages: English
• ISSNs: 0021-8502

Abstract

Abstract: Pulsed laser ablation (PLA) is a widely used technology, for surface structuring and tile decoration in the ceramic industry. During PLA, nanoparticles (NP <100 nm) are unintentionally released and may impact exposure. This work aims to understand the mechanisms controlling NP formation and release during ablation of different types of ceramic tiles, using different laser setups (near-IR and mid-IR). The measurements took place at laboratory and pilot-plant-scale, with varying laser wavelength, frequency, velocity, and pulse duration. In total, the combination of 4 types of ceramic tiles and 2 lasers was assessed. Particle number concentration and size distribution (SMPS with nano-DMA, DiSCmini, butanol-CPC) and particle mass concentration (DustTrak-DRX) were monitored. Samples were also collected for morphological and chemical characterization (TEM/EDX). High particle number concentrations were detected (3.5 *10 4 /cm 3 to 2.5 *10 6 /cm 3 ) for all of the tiles and under both laser setups. Particle formation (<10 nm) by nucleation was detected, and secondary amorphous SiO2 nanoparticles (>10 nm) were formed and released during ablation of the porcelain tiles. Different release mechanisms were identified: during ablation with the near-IR laser particles were emitted through melting and nucleation, while emissions from the mid-IR laser were attributed to melting and mechanical shockwaves. Particle number and mass emissions were dependent on the tile surface characteristics (e.g., porosity, crystallinity) and chemical properties. This work is potentially relevant from the point of view of exposure mitigation strategies in industrial facilities where PLA is carried out. Graphical abstract: fx1 Highlights: Nanoparticles are emitted during laser ablation of ceramic tiles. Main emission routes were nucleation, melting and shockwaves. Tile characteristics and laser parameters determined emissions. Nucleation lead to high particle numbers and shockwaves to high mass concentrations. SiO2 nanoparticles (>10 nm) were formed during porcelain ablation.