Photoluminescence of terbium doped oxyfluoro-titania-phosphate glasses for green light devices. Issue 13 (September 2018)

• Record Type: Journal Article
• Authors: Neelima, G.; Kummara, Venkata Krishnaiah; Viswanath, C.S. Dwaraka; Tyagarajan, K.; Ravi, N.; Prasad, T. Jayachandra
• Is Part Of: Ceramics international. Volume 44:Issue 13(2018)
• Page Start: 15304
• Page End: 15309
• Publication Date: 2018-09
• Subjects: Terbium ions -- Phosphate glasses -- Oxyfluoride glasses -- Photoluminescence -- Decay curves -- Chromaticity color coordinates; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2018.05.176
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Terbium (Tb 3+ ) doped oxyfluoro-titania-phosphate glasses of chemical composition (in mol%), (60 - x) P2 O5 – 15 BaF2 – 20 CaF2 – 5 TiO2 – x Tb4 O7, x = 0.05, 0.1 and 0.1 were fabricated by usual melt-quenching technique. Photoluminescence (PL) properties of the samples have been investigated by excitation, emission and decay profiles. Upon excitation at 377 nm, the PL spectra exhibit an intense band at 541 nm which corresponds to the 5 D4 → 7 F5 transition. The intensity ratio of green-to-blue (IG /IB ) was found to be 9.2 for 0.1 mol% of Tb 3+ -doped glass. High-energy absorption bands were not resolved in the absorption spectrum but disclosed in the photoluminescence excitation spectrum. Decay curves were unveiled non-exponential and mono-exponential behaviours for the 5 D3 and 5 D4 levels, respectively. Lifetime of the 5 D3 and 5 D4 levels was decreased up to 0.1 mol%, and thereafter it was increased with the increase of Tb 3+ ion concentration upon 377 nm excitation. The CIE chromaticity coordinates were supported that the green emission was predominant in Tb 3+ -doped oxyfluoro-titania-phosphate glasses.