The role of TiO2 incorporation in the preparation of B4C/Al laminated composites with high strength and toughness. Issue 13 (September 2018)

• Record Type: Journal Article
• Authors: Yang, Li-Kai; Shen, Ping; Guo, Rui-Fen; Jiang, Qi-Chuan
• Is Part Of: Ceramics international. Volume 44:Issue 13(2018)
• Page Start: 15219
• Page End: 15227
• Publication Date: 2018-09
• Subjects: Boron carbide -- Ice-templating -- Reactive sintering -- Pressure infiltration -- Laminated composites; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2018.05.163
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: We prepared B4 C/Al laminated composites via ice-templating and gas-aided pressure infiltration and investigated the effects of TiO2 addition on the microstructures and mechanical properties of the composites. The incorporation of TiO2 led to the formation of TiB2 after sintering, reduced the formation of harmful phases and increased the strength of ceramic architectures. However, its excessive addition resulted in the cracking of ceramic layers and the formation of metal strips after Al infiltration. The bending strength, fracture toughness and work of fracture of the composites first increased and then decreased with increasing initial TiO2 content, reaching maxima of 420 ± 20 MPa, 44 ± 2 MPa m 1/2 and 5002 ± 175 J m −2, respectively. The specific strength and toughness are comparable to those of titanium alloys. Furthermore, fracture modes and toughening mechanisms were thoroughly addressed by analyzing crack propagation paths and fracture surface morphologies. Crack deflection and metal bridging are two primary extrinsic toughening mechanisms.