Effect of Nanosilica Filled Polyurethane Composite Coating on Polypropylene Substrate. (28th October 2013)

• Record Type: Journal Article
• Authors: Ching, Yern Chee; Syamimie, Nurehan
• Other Names: Qu Mengnan Academic Editor.
• Is Part Of: Journal of nanomaterials. Volume 2013(2013)
• Publication Date: 2013-10-28
• Subjects: Nanostructured materials -- Periodicals; Nanotechnology -- Periodicals; Nanomatériaux; Nanostructured materials; Nanotechnology; Nanostructures; Nanotechnology; Periodicals; Fulltext; Internet Resources; Periodicals; 620.115
• DOI: 10.1155/2013/567908
• Languages: English
• ISSNs: 1687-4110

Abstract

Abstract : Acrylic based polyurethane (PU) coatings with various amounts of nanosilica contents were prepared using solution casting method. The nanosilica (SiO2 ) particles used are around 16 nm in diameter. The friction and wear test was conducted using the reciprocating wear testing machine. The tests were performed at rotary speed of 100 rpm and 200 rpm with load of 0.1 kg to 0.4 kg under 1 N interval. The effect of the PU/nano-SiO2 composite coating on friction and wear behavior of polypropylene substrate was investigated and compared. The worn surface of coating film layer after testing was investigated by using an optical microscope. The introduction of PU/nanosilica composite coating containing 3 wt% of nano-SiO2 content gives the lowest friction coefficient and wear rate to PP substrate. Both the friction and wear rate of PP substrate coated with >3 wt% of nano-SiO2 filled PU coating would increase with the increasing of applied load and sliding time.