In-situ measurement of weld quality during MAG welding using laser ultrasonic. Issue 10 (2nd December 2019)

• Record Type: Journal Article
• Authors: Otaki, Satoshi; Matsuida, Taketo; Nomura, Kazufumi; Imura, Fumiya; Kita, Ryosuke; Asai, Satoru
• Is Part Of: Welding international. Volume 33:Issue 10/11/12(2019)
• Page Start: 450
• Page End: 459
• Publication Date: 2019-12-02
• Subjects: Laser ultrasonic -- in-process monitoring -- non-contacting monitoring -- synthetic aperture focusing technique -- in-situ defect detection -- penetration depth -- weld quality monitoring -- ultrasonic wave.; Welding -- Periodicals; Welding -- Automation -- Periodicals; 671.52
• DOI: 10.1080/09507116.2020.1866361
• Languages: English
• ISSNs: 0950-7116

Abstract

ABSTRACT: Laser ultrasonic technique (LUT) is applicable for measurement under high temperature condition because of the non-contact and remoteness. In this study, LUT was applied to detection the welding defect such as solidification crack and/or lack of penetration at single bevel groove during Gas Metal Arc (GMA) welding process. Nanosecond pulse laser (1064 nm, 60 mJ/pulse 100 Hz) was used to generate ultrasonic, and was scanned using a galvanometer mirror. Nd:YAG laser interferometer (532 nm, 1 W) was used for detection the surface micro vibration caused by arrival of ultrasonic wave. After acquiring the B-scope, which is composed of multi transmit- and receive-points, the synthetic aperture focusing technique (SAFT) is applied. SAFT image obtained by in-process measurement was evaluated to confirm the presence or absence of welding defect indication. As a result, it was possible to indicate the solidification crack and the lack of penetration in the joint even during the welding process. Furthermore, it was able to indicate the penetration depth change (2 mm difference) due to the welding condition change during process. These results suggest that in-process measurement using LUT is very effective technique for detecting weld defects.