Effect of Bi2O3 on phase formation and microstructure evolution of mullite ceramics from mechanochemically activated oxide mixtures. Issue 12 (15th August 2018)

• Record Type: Journal Article
• Authors: Xiao, Zhuohao; Li, Xianglin; Yu, Shijin; Sun, Xinyuan; Li, Xiuying; Wu, Min; Wang, Chuanhu; Zhang, Tianshu; Li, Sean; Kong, Ling Bing
• Is Part Of: Ceramics international. Volume 44:Issue 12(2018)
• Page Start: 13841
• Page End: 13847
• Publication Date: 2018-08-15
• Subjects: Mullite -- Mechanochemistry -- Milling -- Hollow structure; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2018.04.229
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Mullite ceramics with hollow whisker structure have been synthesized firstly through ordinary sintering process. The effects of Bi2 O3 and processing, on mullitization behavior and morphology development of mullite ceramics, derived from the mechanochemically activated mixture of Al2 O3 and SiO2, were investigated in this paper. When the content of Bi2 O3 was less than 10 mol%, the mullite grains show a short rod-like morphology, without the formation of whisker. As the content of Bi2 O3 was increased to more than 10 mol%, the formation temperature of mullite was decreased from 1400 °C to 1100 °C. After sintering at 1400 °C, well-developed mullite whiskers with hollow structure were formed. The formation process and growth mechanism of hollow structural whiskers in mullite ceramic doped with high content of Bi2 O3 were discussed in detail.