Microwave assisted hydrothermal synthesis of (Fe, Co)3O4 nanoparticles in the presence of surfactants and effects of Co/Fe ratio on microstructure and magnetism. Issue 12 (15th August 2018)

• Record Type: Journal Article
• Authors: Ognjanović, Miloš; Dojčinović, Biljana; Fabián, Martin; Stanković, Dalibor M.; Mariano, José F.M.L.; Antić, Bratislav
• Is Part Of: Ceramics international. Volume 44:Issue 12(2018)
• Page Start: 13967
• Page End: 13972
• Publication Date: 2018-08-15
• Subjects: Magnetite -- Microwave synthesis -- Cobalt ferrite -- Structural characterisation -- Magnetic properties; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2018.04.246
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Microstructure and magnetic properties of nanoparticles can be tailored by optimising the synthesis procedure and changing chemical composition. In this study, a two-step procedure, i.e., coprecipitation in the presence of PEG 300 followed by microwave assisted (MW) hydrothermal synthesis, was introduced to obtain Co x Fe3- x O4 ( x = 0, 0.1 and 0.2) nanoparticles. It was found that with the increase of Co content, particle/crystallite size increased, with significant change of coercivity (Hc ). The mixed samples of Co x Fe3- x O4 ( x = 0.1 and 0.2) were magnetically harder in comparison with Fe3 O4 . Тhe Hc of Fe3 O4 was 91 Oe, while for Co0.10 Fe2.90 O4 and Co0.20 Fe2.80 O4, Hc was 256 Oe and 1070 Oe, respectively. Saturation magnetisation (Ms ) of mixed samples also increased up to 6% compared to Fe3 O4 . A special effort was devoted to study the effects of introducing different surfactants (PEG 300, PEG 4000 or SDS) during the synthesis procedure in order to improve morphological and microstructural properties of CoFe2 O4 nanoparticles. The influence of surfactants on physical/chemical properties of nanoparticles is discussed.