Corrosion kinetics study of 316 N weldment under cyclic loading in acidified chloride environment. (2021)

• Record Type: Journal Article
• Authors: Poonguzhali, A.; Ningshen, S.; Amarendra, G.
• Is Part Of: Materials today. Volume 41:Part 5(2021)
• Page Start: 1041
• Page End: 1044
• Publication Date: 2021
• Subjects: Corrosion fatigue -- Nitrogen -- Stainless steel -- Crack initiation -- Corrosion potential -- SEM; Materials science -- Congresses -- Periodicals; 620.1
• DOI: 10.1016/j.matpr.2020.06.569
• Languages: English
• ISSNs: 2214-7853

Abstract

Abstract: Corrosion fatigue crack initiation (CFCI) life of AISI Type 316 N weldment in as-welded (AW) and heat treated (Solution annealed (SA), 550 °C/4h and 750 °C/1h) conditions was studied in high cycle fatigue regime (above 10 4 cycles) with a frequency (η) of 0.1 Hz and and R-ratio (σmin /σmax where σmin and σmax signify minimum and maximum tensile stress in MPa, respectively) of 0.5 for different stress amplitude (σa ) values in boiling acidified 5 M NaCl + 0.15 M Na2 SO4 + 2.5 ml/l HCl solution under axial loading in load controlled mode. In-situ electrochemical measurements were employed during corrosion fatigue tests to study the passive film characteristics. SA weldment showed better corrosion fatigue (CF) resistance as compared to AW and heat treated conditions. Homogenization of microstructural and microchemical heterogeneities facilitates highest resistance to CF cracking process for SA weldment condition. Number of cycles to failure (Nf ) increased with decrease in stress amplitude for all material conditions. CFCI mechanism was identified based on variation in the strain rate (ε°) due to combined effect of both emergence of persistant slip bands (PSBs) casued by rupture of passive film and initiation of microcrack caused by dissolution around depassivation site. The failure of weld metal occurred by a combination of transgranular (TG) and stress-assisted dissolution (SAD) of delta-ferrite. Crack growth zone was minimum for AW and heat treated (550 °C/4h and 750 °C/1h) conditions as compared to SA weldment.