Competitive growth of Si and YSi2 phases in a eutectic Si-Y alloy prepared by the Bridgeman method. Issue 11 (1st August 2018)

• Record Type: Journal Article
• Authors: Li, Jinguang; Hu, Rui; Yang, Jieren; Liu, Yongsheng
• Is Part Of: Ceramics international. Volume 44:Issue 11(2018)
• Page Start: 13232
• Page End: 13239
• Publication Date: 2018-08-01
• Subjects: Si-Y alloy -- Directional solidification -- Eutectic -- Interface growth temperature -- Competitive growth; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2018.04.150
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: A directionally solidified Si-YSi2 alloy was prepared by the Bridgman method at different withdrawal rates. The microstructures of longitudinal section and cross section were investigated. We observed that as the withdrawal rate increased from 0.5 mm/min to 2 mm/min, the morphology of YSi2 phase changed from fine, long strips to islands and finally to blocks distributed along the thick primary Si phase. By calculating the interface growth temperatures of each phase, we found the interface growth temperatures of Si phase and YSi2 phase both decreased with withdrawal rate increasing while that of eutectic structure was almost unchanged. Beyond that the interface growth temperature of Si phase was always higher than that of YSi2 phase. We determined two critical withdrawal rates of V C1 = 0.96 mm/min and V C2 = 1.57 mm/min. Coupled growth was predominant when the withdrawal rate was slower than V C1 and primary Si phase disappeared. Primary Si phase began to form as the withdrawal rate was greater than V C1 and could be obviously thicker as the withdrawal rate was greater than V C2 .