Electrical and magnetic properties of La0.7Ca0.3MnO3 nanoparticle prepared by reactive milling method. (10th March 2021)

• Record Type: Journal Article
• Authors: Thi Dung, Nguyen; Van Dang, Nguyen; Thanh, Tran Dang
• Is Part Of: Advances in natural sciences. Volume 12:Number 1(2021)
• Publication Date: 2021-03-10
• Subjects: manganites -- nanoparticles -- electromagnetic properties; 4.02 -- 5.00 -- 5.02; Nanotechnology -- Periodicals; Nanoscience -- Periodicals; 620.5
• DOI: 10.1088/2043-6262/abeaab
• Languages: English
• ISSNs: 2043-6254

Abstract

Abstract: La0.7 Ca0.3 MnO3 nanoparticle in an orthorhombic structure with space group of Pnma was prepared by a combination of the reactive milling method and annealing at 900 °C for 1 h in air. The mean crystal size determined through the powder x-ray diffraction data is 18 ± 2 nm. Based on the dependences of the resistivity and the magnetisation on temperature and applied magnetic field, the electrical-magnetic properties, the magnetoresistance and the magnetocaloric effects have been investigated. It shows La0.7 Ca0.3 MnO3 nanoparticle undergoes a metal-insulator and a ferromagnetic-paramagnetic phase transitions at T MI = 252 K and T C = 253 K, respectively. The temperature dependences of resistivity of material in the absence and presence of 4 kOe in a range of 30–300 K were fitted to the phase segregation model. The magnetoresistance and the magnetocaloric effects related to the double-exchange interactions taking place around T MI and T C were observed, corresponding to the values of the magnetoresistance MR = 9.29% and the maximum magnetic entropy change ∣Δ S max ∣ = 0.18 J/kg.K under an applied magnetic field of 4 kOe. Besides, the low field magnetoresistance value at low temperature region and the change of the specific heat of La0.7 Ca0.3 MnO3 nanoparticle have also been concerned.