Structural and mechanical properties of lanthanide doped La1/3Nb0.8Ta0.2O3 thin films prepared by sol–gel method. (7th March 2017)

• Record Type: Journal Article
• Authors: Brunckova, Helena; Medvecky, Lubomir; Kovalcikova, Alexandra; Fides, Martin; Mudra, Erika; Durisin, Juraj; Skvarla, Jiri; Kanuchova, Maria
• Is Part Of: Smart materials and structures. Volume 26:Number 4(2017:Apr.)
• Publication Date: 2017-03-07
• Subjects: thin films -- sol–gel -- perovskites -- microstructures -- mechanical properties; Smart materials -- Periodicals; Strucural design -- Periodicals; 620.11
• DOI: 10.1088/1361-665X/aa613c
• Languages: English
• ISSNs: 0964-1726

Abstract

Abstract: Transparent Eu and Nd doped lanthanum niobate tantalate La1/3 Nb0.8 Ta0.2 O3 (LNT) thin films (∼150 nm) were prepared by sol–gel/spin-coating process on Pt/SiO2 /Si substrates and annealing at 1100 °C. The x-ray diffraction analysis of films confirmed formation of the perovskite La1/3 NbO3 and La1/3 TaO3 phases with traces of pyrochlore LaNbO4 . Eu and Nd doped LNT films were smoother with roughness 17.1 and 25.4 nm in comparison with LNT (43.3 nm). In all films was observed heterogeneous microstructure with the perovskite spherical and pyrochlore needle-like particles. The mechanical properties of films were characterized for the first time by conventional and continuous stiffness (CSM) nanoindentation. The Eu and Nd doped LNT film modulus ( E ) and hardness ( H ) were higher than LNT (∼99.8 and 4.4 GPa) determined by conventional nanoindentation. It was measured the significant effect of substrate on properties of Eu or Nd films ( H ∼ 5.9 or 4.9 GPa and E ∼ 107.3 or 104.1 GPa) by CSM nanoindentation.