Dense and core‐rim structured B4C‐TiB2 ceramics with Mo‐Co‐WC additive. Issue 6 (2nd February 2021)

• Record Type: Journal Article
• Authors: Tan, Da‐Wang; Lao, Zhen‐Yong; Zhang, Zhan; Guo, Wei‐Ming; Sun, Shi‐Kuan; Lin, Hua‐Tay
• Is Part Of: Journal of the American Ceramic Society. Volume 104:Issue 6(2021)
• Page Start: 2860
• Page End: 2867
• Publication Date: 2021-02-02
• Subjects: B4C‐TiB2 ceramic -- core‐rim structure -- fracture toughness -- sintering additives -- Vickers hardness; Ceramics -- Periodicals; 620.1405
• DOI: 10.1111/jace.17657
• Languages: English
• ISSNs: 0002-7820

Abstract

Abstract: B4 C‐TiB2 ceramics (TiB2 ranging 5~70 vol%) with Mo‐Co‐WC as the sintering additive were prepared by spark plasma sintering. In comparison with B4 C‐TiB2 without additive, the enhanced densification was evident in the sintered specimen with Mo‐Co‐WC additive. Core‐rim structured grain was observed around TiB2 grains. The interface of the rim between TiB2 and B4 C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B4 C grain. The formation mechanism is discussed: the epitaxial growth of (Ti, Mo, W)B2 rim around the TiB2 core may occur as a result of the solid solution and dissolution‐precipitation between TiB2 phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB2 content increased, alongside the decreased hardness. B4 C‐30 vol% TiB2 specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m 1/2 .