Evaluation and Control of the Molar Mass Bimodality and Properties of Polyethylene from Novel Chromocene‐Based Dual Sites Catalysts. Issue 7 (10th March 2021)

• Record Type: Journal Article
• Authors: Yao, Jiabin; Wang, Kai; He, Xuelian; Liu, Boping
• Is Part Of: Macromolecular chemistry and physics. Volume 222:Issue 7(2021)
• Page Start: n/a
• Page End: n/a
• Publication Date: 2021-03-10
• Subjects: bimodal molecular weight distribution -- dual sites catalysts -- ultrahigh molecular weight polyethylene; Polymers -- Periodicals; Polymerization -- Periodicals; Synthetic products -- Periodicals; Macromolecules -- Periodicals; 547.7
• DOI: 10.1002/macp.202000434
• Languages: English
• ISSNs: 1022-1352

Abstract

Abstract: Polyethylene (PE) with bimodal molecular weight distribution (MWD) has drawn attention from researchers because of its great processability and outstanding mechanical properties. Bimodal PE is successfully prepared by novel SiO2 ‐supported chromocene (S‐9)/chromium (CrO X ) and chromocene (S‐9)/vanadium (V) dual sites catalysts in a single reactor. The molar mass bimodality, crystalline properties, and mechanical properties of the bimodal PE prepared by S‐9/CrO X catalysts are controllable through adjusting the loading of active centers. Those are also adjustable by using S‐9/V catalysts under the condition of adding 0.1 MPa hydrogen. Compared with CrO X /SiO2, 4CrO X 4S9 shows an increase in tensile strength and Young's modulus by 38% and 17%, respectively. With the increase in high MW fraction, tensile strength, and Young's modulus both increase. S‐9/CrO X catalysts combining the advantages of two active centers show better tensile properties. S‐9/V catalysts have a similar trend in tensile properties. The complex viscosity, elastic modulus, and loss modulus increase with the growth in MW and the thickness of lamellae. Furthermore, the high and low MW fraction has good compatibility for both dual sites catalysts, and their resistance to slow crack growth is most likely to reach the standards for PE100 and PE100RC and even exceed. Abstract : The structure and properties of bimodal PE prepared by novel chromocene/inorganic chromium and chromocene/inorganic vanadium dual sites catalysts is systematically investigated. For the bimodal PE, the properties are all been improved to different degrees with the increase of active centers loading which can also be adjusted to change the tensile properties of the PE products.