Variants of the X‐phase in the Mn–Co–Ge system. Issue 4 (9th March 2021)

• Record Type: Journal Article
• Authors: Shtender, Vitalii; Larsen, Simon R.; Sahlberg, Martin
• Is Part Of: Acta crystallographica. Volume 77:Issue 4(2021)
• Page Start: 176
• Page End: 180
• Publication Date: 2021-03-09
• Subjects: intermetallic compound -- crystal structure -- X‐phase -- Mn‐Co‐Ge system -- manganese -- cobalt -- germanide; Crystallography -- Periodicals; Crystals -- Periodicals; 548.3
• DOI: 10.1107/S2053229621002370
• Languages: English
• ISSNs: 2053-2296

Abstract

Abstract : The ordering of two new variants of the X ‐phase derived from the Mn–Co–Ge system is compared with other members of the X ‐phase family and shows that the degree of disordering depends on the chemical composition. No completely ordered variants of the X ‐phase have yet been reported. Abstract : We report two new variants of the X ‐phase (orthorhombic, space group Pnnm ) derived from the Mn–Co–Ge system. Two compositionally related crystals were investigated by means of single‐crystal X‐ray diffraction (XRD) and energy dispersive spectroscopy (EDS). The Mn14.9 Co15.5 Ge6.6 and Mn14 Co16.2 Ge6.8 intermetallic compounds are part of the homogeneity region of the X ‐phase and adopt the Mn14 (Mn0.11 Co0.64 Si0.25 )23 structure type. The composition obtained from refinement of the XRD data is in agreement with the EDS results. In the present study, chemical disorder was only detected on the 8 h positions. The ordering is compared with other members of the X ‐phase family and shows that the degree of disordering depends on the chemical composition. No completely ordered variants of the X ‐phase have yet been reported.