Multi-dimensional ordered mesoporous carbon/silica@Ni composite with hierarchical nanostructure for strong and broadband microwave absorption. (May 2021)

• Record Type: Journal Article
• Authors: Zhou, Panpan; Wang, Xiaokang; Song, Zhi; Wang, Meng; Huang, Wentao; Yu, Mingxun; Wang, Lixi; Zhang, Qitu
• Is Part Of: Carbon. Volume 176(2021)
• Page Start: 209
• Page End: 218
• Publication Date: 2021-05
• Subjects: Ordered mesoporous carbon -- Hierarchical nanostructure -- Magnetoelectric synergy -- Broadband microwave absorption; Carbon -- Periodicals; Carbone -- Périodiques; Koolstof; Toepassingen; Electronic journals; 546.681
• DOI: 10.1016/j.carbon.2021.01.125
• Languages: English
• ISSNs: 0008-6223

Abstract

Abstract: Ordered mesoporous carbon (OMC) has been regarded as a promising carbonaceous material for microwave absorption (MA) owing to its high specific surface area, sufficient ordered mesoporous nanostructures and easy decoration. However, its development in MA performance is seriously hampered by its shortcomings of lacking magnetic loss and poor impedance matching. Herein, a series of multi-dimensional ternary OMC/SiO2 @Ni composites with hierarchical nanostructure (zero-dimensional (0D) Ni nanoparticles and three-dimensional (3D) OMC/SiO2 framework) is successfully prepared via a self-assembly method, an in situ synthesis, and followed by a calcination treatment. By adjusting the calcination temperature and Ni nanoparticle content, OMC/SiO2 @Ni composites with different graphitization degree, Ni nanoparticle size and magnetic properties can be easily obtained. Remarkably, OMC/SiO2 @Ni0.5-700 composite exhibits an exceedingly strong reflection loss (RL) value of −62.2 dB and a broad effective absorption bandwidth (RL ≤ −10 dB) of 8 GHz (almost covers X and Ku bands) with a layer thickness of only 2.5 mm. Such fabulous MA performance comes from a synergy between the well-designed hierarchical ternary nanostructure and improved impedance matching. This work provides an insight for rational structure design and multi-component loss mechanism of lightweight MA material, which shows great potential in practical applications. Graphical abstract: Image 1 Highlights: OMC/Si@Ni composites were successfully fabricated through a self-assembly method and a calcination treatment. Magnetic properties can be tuned through regulating the calcination temperature and compound amount of Ni particles. OMC/Si@Ni0.5-700 achieves strong absorption and broad effective absorption under a thin coating thickness.