Weld defect frequency, size statistics and probabilistic models for ship structures. (April 2021)

• Record Type: Journal Article
• Authors: Amirafshari, Peyman; Barltrop, Nigel; Wright, Martyn; Kolios, Athanasios
• Is Part Of: International journal of fatigue. Volume 145(2021)
• Publication Date: 2021-04
• Subjects: Weld defects -- Cracks size -- Weld defect statistics -- Probabilistic models -- Fracture mechanics; Materials -- Fatigue -- Periodicals; Materials -- Fatigue; Periodicals; 620.1122
• DOI: 10.1016/j.ijfatigue.2020.106069
• Languages: English
• ISSNs: 0142-1123

Abstract

Highlights: Defect statistics for modern ships is given, which is non-existent in public domain. It was found that HLAW process has lower defect rates compared to FCAW and SAW. The probability distributions that best represent defect length data was determined. The welding quality of studied ships was compared to published data from 1980s. Abstract: Ships undergo cyclic loading which combined with weld defects can cause fatigue failure. Remaining fatigue life of structures containing defects can be estimated using the defect size. The defect data for ships is non-existent in literature or belong to old offshore structures. In this research, the data collected from two ships are presented. The statistical analysis of the data shows that the Hybrid Laser Welding has lower defect rates than other common arc welding processes indicating that less quality control inspection may be allowed. The defect length values from the studied ships were smaller than those from offshore structures.