Combining digital image correlation with X-ray computed tomography for characterization of fiber orientation in unidirectional composites. (March 2021)

• Record Type: Journal Article
• Authors: Mehdikhani, Mahoor; Breite, Christian; Swolfs, Yentl; Wevers, Martine; Lomov, Stepan V.; Gorbatikh, Larissa
• Is Part Of: Composites. Volume 142(2021)
• Publication Date: 2021-03
• Subjects: A. Fibers -- D. CT analysis -- D. Microstructural analysis -- Digital image correlation; Composite materials -- Periodicals; Manufacturing processes -- Periodicals; Composite materials; Manufacturing processes; Periodicals; 620.11805
• DOI: 10.1016/j.compositesa.2020.106234
• Languages: English
• ISSNs: 1359-835X

Abstract

Abstract: We apply Digital Image Correlation (DIC) to X-ray Computed Tomography (CT) slices for characterization of individual fibers misalignment in continuous fiber composites. This is an atypical application of DIC since the input is slices of a CT tomogram acquired at one time step, whereas the input of the typical deformation analysis application is 2D images captured over consecutive loading steps. The methodology is demonstrated and validated on synchrotron CT images of a glass/epoxy laminate, where individual fibers can be clearly identified. It is found that the average/standard deviation of the DIC displacement field in every CT slice is a good estimation of the average/standard deviation of the actual displacement of all fibers' cross-sections in that slice. This provides a shortcut to the measurement of the moments of fiber orientation distribution, compared to the algorithms that reconstruct the fiber center lines. Using this shortcut, the fiber misalignment was also characterized in synchrotron CT images of a carbon/epoxy laminate, where individual fibers were not clearly observed and where, fiber segmentation tools failed to characterize the fibers. Furthermore, being applied to synchrotron images acquired during in-situ tension, the methodology is employed to quantify the evolution of misalignment during tension. The investigated 3D volumes are provided in [1] and described in [2].