Contact between Garnet-Type Solid Electrolyte and Lithium Metal Anode: Influence on Charge Transfer Resistance and Short Circuit Prevention. Issue 4 (3rd February 2017)

• Record Type: Journal Article
• Authors: Basappa, Rajendra Hongahally; Ito, Tomoko; Yamada, Hirotoshi
• Is Part Of: Journal of the Electrochemical Society. Volume 164:Issue 4(2017)
• Page Start: A666
• Page End: A671
• Publication Date: 2017-02-03
• Subjects: All Solid-State Battery -- Charge Transfer Resistance -- Garnet -- Interface -- Li Electrode -- Short Circuit; Electrochemistry -- Periodicals; 541.3705
• DOI: 10.1149/2.0841704jes
• Languages: English
• ISSNs: 0013-4651

Abstract

Abstract : Interface structure between Li and garnet-type Li6.5 La3 Zr1.5 Ta0.5 O12 (LLZT) solid electrolyte was investigated by means of electrochemical impedance spectroscopy (EIS) on symmetric cells of Li | LLZT | Li. Charge transfer resistance ( R CT ) between Li and LLZT was investigated using LLZT pellets with various roughness. R CT and activation energy ( E a ) obtained on the flat interface is as high as 746 Ω cm 2 and 0.51 eV at 25°C, respectively, indicating that the charge transfer reaction at Li | LLZT (grit number: #8000) interface is a kinetically slow process, which may suppress rate capability of all solid-state batteries. Although the lowest R CT of 363 Ω cm 2 was obtained by heating up to the melting point of Li for the LLZT pellet polished with an emery paper (#400), it is supposed that electrochemically effective contact area was saturated for rougher surfaces of LLZT. To prepare interfaces with large effective contact area, Li electrodes were deposited on a LLZT pellet by vacuum-evaporation, which exhibited further low R CT of 69 Ω cm 2 . The interface with large effective contact area is also a key to prevention of short circuit, and a high critical current density of 0.4 mA cm −2 was demonstrated.