Durability Failure Analysis of Proton Exchange Membrane Fuel Cell and Its Effect on Oxygen Transport in Gas Diffusion Layer. Issue 13 (6th September 2019)

• Record Type: Journal Article
• Authors: Pang, Jin; Li, Shang; Wang, Ruyi; Zhu, Kai; Liu, Shengchu; Guo, Zhi; Pan, Mu
• Is Part Of: Journal of the Electrochemical Society. Volume 166:Issue 13(2019)
• Page Start: F1016
• Page End: F1021
• Publication Date: 2019-09-06
• Subjects: Fuel Cells - PEM -- gas diffusion layer -- oxygen transport resistance -- proton exchange membrane fuel cells; Electrochemistry -- Periodicals; 541.3705
• DOI: 10.1149/2.1101913jes
• Languages: English
• ISSNs: 0013-4651

Abstract

Abstract : The poor durability of proton exchange membrane fuel cells still is their greatest barrier preventing commercialization. In this paper, we perform a 1465 h in situ durability test with a single fuel cell operating at a constant-current of 800mA cm −2 . Polarization curves, cyclic voltammetry, and electrochemical impedance spectroscopy are used for diagnostics and to understand changes in performance during the test. Limiting current method is used to analyze the oxygen transport resistance of the gas diffusion layer (GDL) before and after durability test. The results indicate that the oxygen transport resistance in single cell increases greatly, and GDL is the first component leading to fuel cell failure after1465h test. At 150 kPa and 20% dry oxygen mole fraction, the limiting current decreases to about 700mA cm −2 and total oxygen transport resistance increases by 0.1623s cm −1, implying more serious flooding occurs in GDL after the 1465 h durability test. The increase of oxygen transport resistances of the substrate and micro porous layer of GDL confirm the loss of water management capability of GDL. SEM images show that these may be caused by oxidation of carbon and loss of polytetrafluoroethylene in GDL.