Enhanced flow boiling heat transfer on chromium coated zircaloy-4 using cold spray technique for accident tolerant fuel (ATF) materials. (25th February 2021)

• Record Type: Journal Article
• Authors: Lee, Donghwi; Elward, Barret; Brooks, Paul; Umretiya, Rajnikant; Rojas, Jessika; Bucci, Matteo; Rebak, Raul B.; Anderson, Mark
• Is Part Of: Applied thermal engineering. Volume 185(2021)
• Publication Date: 2021-02-25
• Subjects: Flow boiling heat transfer -- Accident tolerant fuel -- Chromium coated zirconium -- Void fraction -- Shadowgraph; Heat engineering -- Periodicals; Heating -- Equipment and supplies -- Periodicals; Periodicals; 621.40205
• DOI: 10.1016/j.applthermaleng.2020.116347
• Languages: English
• ISSNs: 1359-4311

Abstract

Highlights: Flow boiling tests were performed on Zr4 and chromium coated Zr4 (PVD and cold spray). Temperature profile was evaluated by distributed high-resolution optic sensors. Void fraction was analyzed by shadowgraph images using high-speed visualization. HTC was 5.2% enhanced on coated Zr4 (cold spray) owing to high void fractions. Whereas CHF was 10.1% lowered by formation of vapor film from high void fraction. Abstract: Flow boiling heat transfer tests were conducted to evaluate the Critical Heat Flux (CHF) and Heat Transfer Coefficient (HTC) of conventional and accident tolerant fuel (ATF) cladding materials, i.e., bare Zircaloy-4 (Zr4), and Zircaloy-4 coated with Chromium using physical vapor deposition (PVD) (Zr4-Cr-PVD) and cold spray process (Zr4-Cr-CS), respectively. The tests were performed on a single heater rod with a uniform heat flux profile, at the atmospheric pressure, inlet temperature (24 °C) and mass flow rate (750 kg/m 2 s). HTC's were increased by 5.2% and 3.3% on Zr4-Cr-CS compared to bare Zr4 and Zr4-Cr-PVD. Improved HTCwas attributed to the increased void fraction and high roughness (Ra = 532 nm) of the Zr4-Cr-CS. In detail, the micro-cavities, which act as bubble seeds, were entirely distributed on the Zr4-Cr-CS, and these micro-cavities generated smaller and faster bubbles, thus the void fraction increased by 10.9% compared to bare Zr4. HTC is improved by these smaller and faster bubbles which can remove heat from the heater rod surface more efficiently. To identify the exact location of CHF, the surface temperature profile was measured using advanced fiber-optic sensors which have high temporal/spatial resolution (distance between point to point: ~2.5 mm, frequency ~100 Hz). CHF occurred at 80–95% along the heated length and showed an 11.6% reduction on Zr4-Cr-CS compared to bare Zr4. We hypothesize the CHF reduction was caused by the lower wettability of the Zr4-Cr-CS which reduces the liquid supply to the surface, and vigorous bubble accumulation owing to high void fraction near the outlet, which results in early formation of the vapor film. During the post-CHF quenching phase, the rougher Zr4-Cr-CS showed larger cooling rates compared to the bare Zr4 and Zr4-Cr-PVD, preventing of oxidation by chromium layer. In conclusion, we demonstrate that the high roughness on the Zr4-Cr-CS increased the number of micro-cavities on the surface, resulting in 5.2% increase in HTC and improvement in the quenching heat transfer performance whereas CHF was 11.6% reduced compared to bare Zr4. Overall statistically there is little effect in the coating with regards to CHF and slight improvement in HTC.