Hydrogen transport property of polymer-derived cobalt cation-doped amorphous silica. Issue 1 (5th November 2020)

• Record Type: Journal Article
• Authors: Tada, Shotaro; Ando, Shiori; Asaka, Toru; Daiko, Yusuke; Honda, Sawao; Bernard, Samuel; Iwamoto, Yuji
• Is Part Of: Inorganic chemistry frontiers. Volume 8:Issue 1(2021)
• Page Start: 90
• Page End: 99
• Publication Date: 2020-11-05
• Subjects: Chemistry, Inorganic -- Periodicals; 546.05
• DOI: 10.1039/d0qi01035a
• Languages: English
• ISSNs: 2052-1553

Abstract

Abstract : The effect of the local structure of Co-doped amorphous silica on the hydrogen transport property was studied with the aim to improve the high-temperature hydrogen-permselectivity of microporous amorphous silica-based membranes. Abstract : The effect of the local structure of Co-doped amorphous silica on the hydrogen transport property was studied with the aim to improve the high-temperature hydrogen-permselectivity of microporous amorphous silica-based membranes. Co-Doped silica materials with measured Co/Si atomic ratios ranging from 0.01 to 0.18 were successfully synthesized through the polymer-derived ceramic (PDC) route. X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) analyses confirmed the amorphous state of the polymer-derived Co-doped silica, while both X-ray photoelectron and Fourier transform infrared (FT-IR) spectroscopy analyses revealed that the divalent Co cation (Co 2+ ) modified the matrix amorphous silica network to form hydrogen-bonded silanol. After dehydration treatment at 500 °C in argon, hydrogen (H)/deuterium (D) isotope exchange behavior on the surface silanol groups (Si–OH/OD conversion) of the polymer-derived non-doped and Co-doped amorphous silica was in situ monitored by measuring diffuse reflectance infrared Fourier transform (DRIFT) spectra at 500 °C. The self-diffusion coefficient for OH/OD conversion of free silanol groups of non-doped silica was 6.1 × 10 −15 m 2 s −1, while that on the hydrogen bonded Si–OH was found to reach 15.6 × 10 −15 m 2 s −1 by Co-doping at the measured Co/Si atomic ratio of 0.05.The effect of the amount of Co 2+ doping on the hydrogen transport property was further studied by scanning transmission electron microscopy and electron energy loss spectroscopy (STEM-EELS) analyses, and it was suggested that a rather small amount of Co-doping, i.e. Co/Si atomic ratio of 0.05 was effective for enhancing high-temperature hydrogen permeance through microporous amorphous silica-based membranes.