Co-Cr-Mo-Cu alloys for clinical implants with osteogenic effect by increasing bone induction, formation and development in a rabbit model. Issue 1 (21st December 2020)

• Record Type: Journal Article
• Authors: Duan, Jingzhu; Yang, Yang; Zhang, Erlin; Wang, Huan
• Is Part Of: Burns and trauma. Volume 8:Issue 1(2020)
• Publication Date: 2020-12-21
• Subjects: Co-Cr-Mu-Cu alloy -- Cu ion -- Osteogenic capability -- Implantable operation -- Clinical application; Burns and scalds -- Periodicals; Wounds and injuries -- Periodicals; 617.11
• DOI: 10.1093/burnst/tkaa036
• Languages: English
• ISSNs: 2321-3876

Abstract

Abstract: Background: Co-Cr-Mo alloy has been widely used in clinical implants because of its excellent mechanical and anti-corrosion properties, but there is an urgent need to address its disadvantages, such as implant-related infections and implant loosening. We synthesized Co-Cr-Mo-Cu (Co-Cu) alloys with different Cu contents to modify implant performance to be suitable as a bone-compatible implant material. Methods: Microstructure, phase content and mechanical properties of the Co-Cr-Mo alloy were characterized. Histological and immunohistochemical analyses were performed after implantation in rabbits. The experimental alloy was implanted on the lateral side of the lower tibial condyle and the tibial nodule. Results: Phase content and mechanical properties revealed that the crystallographic structure and wear resistance were changed. Experimental implantation results demonstrated that osteogenic capability was markedly enhanced, ascribed to the excellent antibacterial and osseointegration capacities of Cu phases, and with the release of Cu ions. In particular, Co-Cu alloy containing 2 wt% Cu exhibited the best osteogenic performance among all samples. Conclusions: The results indicated that osteogenic performance of the Co-Cr-Mo alloy could be enhanced by adding Cu. In particular, the Co-2Cu alloy exhibited the best properties according to both immunohistochemical and histological analyses. Our study not only provides deep insight into the osteogenic effect of Cu but presents a new Co-Cu alloy for clinical implants.