Experimental investigation and thermodynamic description of the Ni–Ti–W system. (December 2020)

• Record Type: Journal Article
• Authors: Du, Zeting; Hu, Die; Guo, Cuiping; Ren, Xueping; Li, Changrong
• Is Part Of: Calphad. Volume 71(2020)
• Publication Date: 2020-12
• Subjects: Ni–Ti–W system -- Liquidus surface projection -- Isothermal sections -- CALPHAD method; Phase diagrams -- Data processing -- Periodicals; Thermochemistry -- Data processing -- Periodicals; Diagrammes de phases -- Informatique -- Périodiques; Thermochimie -- Informatique -- Périodiques; Thermodynamica; Electronic journals; 541.363
• DOI: 10.1016/j.calphad.2020.102194
• Languages: English
• ISSNs: 0364-5916

Abstract

Abstract: The liquidus surface projection and isothermal sections at 1173 and 1373 K of the Ni–Ti–W system were constructed on the basis of microstructure and phase constituents of as-cast and annealed alloys, which were obtained by means of scanning electron microscopy (SEM) coupled with energy dispersion spectroscopy (EDS), X–ray diffraction (XRD). Six primary solidification regions were determined in the liquidus surface projection. Five and six three-phase regions were derived in the isothermal sections at 1173 and 1373 K, respectively. No new ternary compounds were found. Based on the present experimental data, the Ni–Ti–W system was optimized using CALPHAD (CALculation of PHase Diagram) method. The solution phases, liquid, fcc, bcc, and hcp, were treated as substitutional solution. Two compounds Ni3 Ti and NiTi2 were treated as (Ni, Ti, W) m (Ni, Ti, W) n, and Ni4 W was treated as (Ni, Ti)4 W1 by a two-sublattice model. NiTi with B2 crystal structure was treated as the ordered phase of bcc solution, and model was (Ni, Ti, W)0.5 (Ni, Ti, W)0.5 (Va)3 . A set of self-consistent thermodynamic parameters was obtained. Highlights: The liquidus projection in the Ni–Ti–W system was investigated by SEM/EDS and XRD. Two isothermal sections at 1173 and 1373 K in the Ni–Ti–W system were determined. The Ni–Ti–W system was optimized by means of CALPHAD method.