A recyclable vanillin-based epoxy resin with high-performance that can compete with DGEBA. (5th November 2020)

• Record Type: Journal Article
• Authors: Su, Xunzheng; Zhou, Zhen; Liu, Jingcheng; Luo, Jing; Liu, Ren
• Is Part Of: European polymer journal. Volume 140(2020)
• Publication Date: 2020-11-05
• Subjects: Vanillin -- Dynamic covalent bond -- Epoxy resin -- Reprocessing; Polymers -- Periodicals; Polymerization -- Periodicals; Polymères -- Périodiques; Polymérisation -- Périodiques; Polymerization; Polymers; Periodicals; Electronic journals; 547.705
• DOI: 10.1016/j.eurpolymj.2020.110053
• Languages: English
• ISSNs: 0014-3057

Abstract

Graphical abstract: A vanillin-based epoxy resin with excellent mechanical, thermal properties and recyclability after cued by primary amine. Highlights: A vanillin-based epoxy resin with excellent properties and reprocessability. The imine bonds can be formed in situ during curing with primary amine. An idea for the synthesis of recyclable crosslinked polymers was provided. Abstract: In this paper, a high-performance epoxy resin was synthesized from vanillin, and the polyimine-epoxy cross-linked network was prepared via in-situ formation of the Schiff base structure. The chemical structures, thermal and mechanical properties of vanillin-based epoxy resin (DADE) and diglycidyl ether of bisphenol A epoxy resin (DGEBA) were characterized by fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance spectra ( 1 H NMR), differential scanning calorimetry (DSC), and dynamic thermomechanical analysis (DMA). The results indicated that the DADE showed better thermal and mechanical properties than DGEBA after cured by the same primary amine (D230). The prepared DADE-D230 showed higher Tg (106℃), tensile strength (57.4 MPa) and elongation at break (3.1%) than DGEBA-D230 (98℃, 45.1 MPa, and 2.4%, respectively). Moreover, it can be recycled at a hot pressing, and the reprocessed samples showed a comparable performance with DGEBA.