Impact of backbone composition on homopolymer dynamics and brush block copolymer self-assembly. Issue 45 (1st October 2020)

• Record Type: Journal Article
• Authors: Boyle, Bret M.; Collins, Joseph L.; Mensch, Tara E.; Ryan, Matthew D.; Newell, Brian S.; Miyake, Garret M.
• Is Part Of: Polymer chemistry. Volume 11:Issue 45(2020)
• Page Start: 7147
• Page End: 7158
• Publication Date: 2020-10-01
• Subjects: Polymers -- Periodicals; Macromolecules -- Periodicals; Polymerization -- Periodicals; 547.705
• DOI: 10.1039/d0py01007c
• Languages: English
• ISSNs: 1759-9954

Abstract

Abstract : Four series of brush block copolymers with near identical side chain compositions but varying backbone structures were synthesized to investigate the effect of backbone structure on the thermal self-assembly to photonic crystals. Abstract : Four series of brush block copolymers (BBCP), with near identical side chain compositions but varying backbone structures, were synthesized to investigate the effect of backbone structure on the process of thermal BBCP self-assembly to photonic crystals (PCs). Each of the self-assembled PC films was examined by reflection measurements, small angle X-ray scattering measurements, and scanning electron microscopy to compare the resulting properties of the polymeric photonic crystal and the nanostructured morphology impacted by the backbone structure. It was found that the composition of the brush backbone within a BBCP has a dramatic effect on the ability of the BBCP to self-assemble into ordered nanostructures and on the local ordering of the nanostructure morphology accessed with higher molecular weight (MW) BBCPs (>1500 kg mol −1 ). BBCPs with a norbornene imide-based backbone were able to thermally self-assemble to longer wavelength reflecting PCs and had higher fidelity ordering of lamellar nanostructures with higher MW polymers. By analyzing the melt rheological responses of the backbone compositions, both as linear polymers and homobrush polymers, it was concluded that the inherent fragility of the backbone promotes enhanced local ordering in the lamellar nanostructure morphology as well as access to larger domain sizes.