Fabrication of inverted pyramid structure by Cesium Chloride self-assembly lithography for silicon solar cell. (December 2015) - Liu, Jing
Abstract: Inverted pyramids were fabricated through a method combining cesium chloride (CsCl) self-assembly technology and anisotropy corrosion of silicon solar cells. Ti film with nanoporous masks was formed by lift-off the CsCl nanoislands for the inverted pyramids. The pyramids were then formed by anisotropy corrosion of alkaline solution. The average diameter and morphology of the pyramids were controlled by varying the average diameter of CsCl nanoislands from 400 nm to 1.5 µm and by varying the etching time of alkaline solution from 2 to 8 min. The inverted-pyramid texture could suppress reflection to below 10% at wavelengths from 400 to 1000 nm, which was much lower than that of planar wafer. A solar cell fabricated from the pyramids had higher short-circuit current density ( J sc ) and photovoltaic conversion efficiency (PCE) compared with those of planar solar cells for the good antireflection property. The solar cell showed a PCE of 15.25%, a J sc of 38.35 mA/cm 2, and an open-circuit voltage of 555.7 mV.